MOS-41; Methyl Phenyl Reactive Silicone Intermediate

Special features

  • low viscous methoxy-functional silicone intermediate
  • solvent-free
  • curing at ambient temperature by catalysis and with humidity via a hydrolysis-/condensation reaction
  • very low odor development of the completely cured coating

Technical information

  • delivery form liquid
  • appearance clear liquid
  • active matter content 99 %
  • viscosity at 25 °C approx. <5 – mPa s
  • methoxy content approx. 37 wt-%

Application

  • high temperature application for industrial facilities,
  • anti-corrosion coatings (depending on formulation)

Processing instructions

  • Use with metallic pigments to obtain continuous heat-resistance of up to 600 °C.
  • Forced drying, is only possible in presence of air humidity. The cross-linking proceeds via a hydrolysis/condensation reaction.
  • The addition of the catalyst TnBT must be carried out just before filling (1K system) or just before the application (2K system).
  • add water scavenger at an amount of < 0.75%.
  • Recommended addition level of the catalyst 1 – 3% calculated on binder
  • Check the storage stability of the formulation.
  • Recommended dry film thickness: 25 μm

Dilution

Dilution is possible with organic solvents, e.g. aromatic, esters, alcohols and ketones.

Curing conditions

  • dust-dry at ambient temperature (23 °C) after 1 – 2 hours
  • reaches full cure and full mechanical strength after 14-21 days

Registration status

MOS-41 respectively its ingredients are listed in the following chemical inventories: AICS, ECL, EINECS, ENCS, IECSC,

NDSL, PICCS, TSCA, NZIOC, TCSI.

All intentional ingredients are listed on the TSCA inventory or comply with the TSCA Polymer Exemption criteria according 40 CFR 723.

Further information on regulatory topics can be found on the Regulatory Data Sheet.

All intentional ingredients are listed on the ECL inventory or comply with the Polymer Exemption criteria.

All intentional ingredients are listed on the PICCS inventory or comply with the Polymer Exemption criteria.

Storage stability

When stored in an original unopened packaging between -15 and +30°C, the product has a shelf life of at least 24 months from the date of manufacture.